- 密度 [g/cm3]: 1.1
- 缺口冲击强度: 18.0
- 拉伸强度 [MPa]: 63.5
- 弯曲模量 [MPa]: 2.28
- 热变形温度 [℃]: 192.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 63.5 MPa | 9210 psi | 50mm/min; ISO 527 | ||
| Elongation at Break | 28 % | 28 % | 50mm/min, Nominal strain; ISO 527 | ||
| Elongation at Yield | 6.2 % | 6.2 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 2.44 GPa | 354 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 2.28 GPa | 331 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 18.0 kJ/m² | 8.57 ft-lb/in² | ISO Test | ||
| 12.0 kJ/m² @Temperature -40.0 °C | 5.71 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact, Notched | 1.90 J/cm² | 9.04 ft-lb/in² | ISO 179 | ||
| 1.40 J/cm² @Temperature -30.0 °C | 6.66 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 262 °C | 504 °F | 10 K/min | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 192 °C | 378 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||