- 密度 [g/cm3]: 1.13
- 缺口冲击强度: 6.0
- 拉伸强度 [MPa]: 85.0
- 弯曲模量 [MPa]: 2.92
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 4.3 % | 4.3 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 3.12 GPa | 453 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 2.92 GPa | 424 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO Test | ||
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | 10 K/min | ||
| 260 °C | 500 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C | 165 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||