- 熔体流动速率 [g/10min]: 40.0
- 密度 [g/cm3]: 1.34
- 吸水率 [%]: 6.0
- 缺口冲击强度: 7.0
- 弯曲强度 [MPa]: 115.0
- 弯曲模量 [MPa]: 6.90
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.0 % | 6.0 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | 23°C/50% R.H.; ISO 62 | ||
| Melt Flow | 40 g/10 min @Load 5.00 kg, Temperature 275 °C | 40 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 115 MPa | 16700 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| Flexural Modulus | 6.90 GPa | 1000 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | ISO Test | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Strength | 33.0 kV/mm | 838 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | 10 K/min | ||
| 260 °C | 500 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75 | ||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |||
| V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | ||||
| 5VA @Thickness 3.00 mm | 5VA @Thickness 0.118 in | ||||
| Descriptive Properties | |||||
| Color | BK23187 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||