- 熔体流动速率 [g/10min]: 73.8
- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 6.7
- 缺口冲击强度: 5.6
- 拉伸强度 [MPa]: 85.0
- 弯曲模量 [MPa]: 4.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |||
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.7 - 7.3 % | 6.7 - 7.3 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.9 - 2.5 % | 1.9 - 2.5 % | 23°C; 50% RH; ISO 62 | ||
| 2.2 % | 2.2 % | 50% RH; ISO 62 | |||
| 7.0 % | 7.0 % | Saturation; ISO 62 | |||
| Viscosity Measurement | 145 | 145 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0075 cm/cm | 0.0075 in/in | restricted | ||
| Melt Flow | 73.8 g/10 min @Load 5.00 kg, Temperature 275 °C | 73.8 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 10 % | 10 % | 50mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 4.50 GPa | 653 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 125 MPa | 18100 psi | at max force; ISO 178 | ||
| Flexural Modulus | 4.00 GPa | 580 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.60 kJ/m² @Temperature 23.0 °C | 2.66 ft-lb/in² @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 7.00 J/cm² @Temperature 23.0 °C | 33.3 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.10 J/cm² @Temperature 23.0 °C | 5.23 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Tensile Creep Modulus, 1000 hours | 2600 MPa @Strain <=0.500 % | 377000 psi @Strain <=0.500 % | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 5.5 @Frequency 1.00 Hz | 5.5 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.30 @Frequency 1.00e+6 Hz | 0.30 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 450 V | 450 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 260 °C | 500 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20000hr | ||
| 175 °C | 347 °F | for 50% loss of tensile strength after 5000hr | |||
| 240 °C | 464 °F | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 290 °C | 554 °F | Feed zone | ||
| Zone 2 | 290 °C | 554 °F | Compression | ||
| Zone 3 | 290 °C | 554 °F | Metering-zone | ||
| Zone 4 | 290 °C | 554 °F | Nozzle | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection-molding/Extrusion | ||
| 290 °C | 554 °F | Optimal | |||
| Mold Temperature | 80.0 °C | 176 °F | Optimal | ||
| 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Color | BK 00564 | ||||
| Commercial Status | Europe and North America | ||||
| Peripheral Screw Speed | < 0.3 m/s | ||||