- 熔体流动速率 [g/10min]: 42.6
- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 4.0
- 缺口冲击强度: 8.0
- 拉伸强度 [MPa]: 100.0
- 弯曲模量 [MPa]: 9.80
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 | ||
| Water Absorption | 4.0 - 4.6 % | 4.0 - 4.6 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.1 - 1.5 % | 1.1 - 1.5 % | 23°C; 50% RH; ISO 62 | ||
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | restricted | ||
| Melt Flow | 42.6 g/10 min @Load 5.00 kg, Temperature 275 °C | 42.6 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 100 MPa | 14500 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 2.8 % | 2.8 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 10.0 GPa | 1450 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 220 MPa | 31900 psi | at max force; ISO 178 | ||
| Flexural Modulus | 9.80 GPa | 1420 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature 23.0 °C | 3.81 ft-lb/in² @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -30.0 °C | 21.4 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 6.00 J/cm² @Temperature 23.0 °C | 28.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.700 J/cm² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00 Hz | 3.8 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.017 @Frequency 1.00e+6 Hz | 0.017 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 21.0 - 23.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 11.7 - 12.8 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 70.0 - 100 µm/m-°C @Temperature 23.0 - 80.0 °C | 38.9 - 55.6 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Melting Point | 260 °C | 500 °F | DIN 53765 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-2 @Thickness >=0.400 mm | V-2 @Thickness >=0.0157 in | |||
| 5VA @Thickness >=1.60 mm | 5VA @Thickness >=0.0630 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||