- 熔体流动速率 [g/10min]: 157.2
- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 6.6
- 缺口冲击强度: 4.0
- 拉伸强度 [MPa]: 95.0
- 弯曲模量 [MPa]: 5.70
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.6 - 7.2 % | 6.6 - 7.2 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.0 - 2.4 % | 2.0 - 2.4 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 150 | 150 | ISO 307 | ||
| Melt Flow | 157.2 g/10 min @Load 5.00 kg, Temperature 275 °C | 157.2 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 3.0 % | 3.0 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 6.00 GPa | 870 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 150 MPa | 21800 psi | at max force; ISO 178 | ||
| Flexural Modulus | 5.70 GPa | 827 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | ISO 180/A | ||
| 5.00 kJ/m² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | ISO 180/A | |||
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature -30.0 °C | 16.7 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 4.00 J/cm² @Temperature 23.0 °C | 19.0 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.300 J/cm² @Temperature 23.0 °C | 1.43 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| 0.340 J/cm² @Temperature -30.0 °C | 1.62 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00 Hz | 3.8 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.015 @Frequency 1.00e+6 Hz | 0.015 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 50.0 - 55.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 27.8 - 30.6 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 50.0 - 60.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 27.8 - 33.3 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | |||
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 160 °C | 320 °F | for 50% loss of tensile strength after 20000hr | ||
| 185 °C | 365 °F | for 50% loss of tensile strength after 5000hr | |||
| 200 °C | 392 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-2 @Thickness >=0.710 mm | V-2 @Thickness >=0.0280 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | BK 23215 | ||||
| Commercial Status | Europe | ||||