  4. Bond Laminates TEPEX® dynalite 201-C200(x)/45% Carbon – PA6.6 Consolidated Composite Laminate

Bond Laminates TEPEX® dynalite 201-C200(x)/45% Carbon – PA6.6 Consolidated Composite Laminate

Bond Laminates TEPEX® dynalite 201-C200(x)/45% Carbon – PA6.6 Consolidated Composite Laminate 物性表: Bond Laminates TEPEX® dynalite 201-C200(x)/45% Carbon – PA6.6 Consolidated Composite Laminate物性表及特性介绍,Bond Laminates TEPEX® dynalite 201-C200(x)/45% Carbon – PA6.6 Consolidated Composite Laminate注塑参数详情,如需Bond Laminates TEPEX® dynalite 201-C200(x)/45% Carbon – PA6.6 Consolidated Composite Laminate下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.43
  • 弯曲模量 [MPa]: 44.1
 
Physical PropertiesMetricEnglishComments
Density 1.43 g/cc0.0517 lb/in³
Filler Content 45 %45 %by volume
Thickness 250 microns9.84 millaminate layer thickness
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength 725 MPa105000 psitransverse; ISO 527-4/5
 785 MPa114000 psilongitudinal; ISO 527-4/5
Elongation at Break 2.1 %2.1 %longitudinal; ISO 527-4/5
 2.1 %2.1 %transverse; ISO 527-4/5
Tensile Modulus 51.0 GPa7400 ksitransverse; ISO 527-4/5
 53.0 GPa7690 ksilongitudinal; ISO 527-4/5
Flexural Strength 730 MPa106000 psitransverse; ISO 178
 760 MPa110000 psilongitudinal; ISO 178
Flexural Modulus 44.1 GPa6400 ksitransverse; ISO 178
 45.5 GPa6600 ksilongitudinal; ISO 178
Poissons Ratio 0.0700.070longitudinal; ISO 527-4/5
 0.0700.070transverse; ISO 527-4/5
Charpy Impact Unnotched  11.0 J/cm²
@Temperature 23.0 °C		52.3 ft-lb/in²
@Temperature 73.4 °F		longitudinal; ISO 179/1eU
 15.0 J/cm²
@Temperature -30.0 °C		71.4 ft-lb/in²
@Temperature -22.0 °F		longitudinal; ISO 179/1eU
 
Thermal PropertiesMetricEnglishComments
Melting Point 260 °C500 °FDSC 3146
Maximum Service Temperature, Air 130 °C
@Time 7.20e+7 sec		266 °F
@Time 20000 hour		Relative Temperature Index; IEC 216/1
Deflection Temperature at 1.8 MPa (264 psi) 255 °C491 °FISO 75-1/2
Minimum Service Temperature, Air -30.0 °C-22.0 °F
Glass Transition Temp, Tg 70.0 °C158 °FDSC 3146
 
Processing PropertiesMetricEnglishComments
Processing Temperature 280 - 300 °C536 - 572 °F
 
Descriptive Properties
ReinforcementArea weight200 g/m²
 Fabrictwill 2/2
 Fiberscarbon
 Weight Rate50% longitudinal and transverse
 Yarn3000 tex longitudinal and transverse

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45166.html

免责声明: 本文 Bond Laminates TEPEX® dynalite 201-C200(x)/45% Carbon – PA6.6 Consolidated Composite Laminate 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络