- 密度 [g/cm3]: 1.23
- 缺口冲击强度: 0.534
- 弯曲模量 [MPa]: 4.96
- 硬度: 121.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Filler Content | 13 % | 13 % | |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength at Break | 117 MPa | 17000 psi | ASTM D638 |
| Elongation at Break | 4.5 % | 4.5 % | ASTM D638 |
| Flexural Strength | 165 MPa | 24000 psi | ASTM D790 |
| Flexural Modulus | 4.96 GPa | 720 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 261 °C | 501 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 241 °C | 465 °F | Unannealed; ASTM D648 |