- 密度 [g/cm3]: 1.19
- 缺口冲击强度: 1.33
- 断裂伸长率 [%]: 124
- 弯曲强度 [MPa]: 90.0
- 弯曲模量 [MPa]: 3.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | ASTM D638 |
| Elongation at Break | 4.6 % | 4.6 % | ASTM D638 |
| Flexural Yield Strength | 124 MPa | 18000 psi | ASTM D790 |
| Flexural Modulus | 3.80 GPa | 551 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 279 °C | 534 °F | |