- 缺口冲击强度: 0.53
- 拉伸强度 [MPa]: 83.0
- 弯曲模量 [MPa]: 2.86
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.013 cm/cm @Thickness 3.17 mm | 0.013 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D882 |
| Flexural Modulus | 2.86 GPa | 415 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 0.993 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |