- 密度 [g/cm3]: 1.45
- 缺口冲击强度: 5.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 40 % | 40 % | DAM | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 59.0 MPa @Temperature 23.0 °C | 8560 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 87.0 MPa @Temperature 23.0 °C | 12600 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 8.0 % @Temperature 23.0 °C | 8.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 20 % @Temperature 23.0 °C | 20 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 2.50 GPa @Temperature 23.0 °C | 363 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 5.80 GPa @Temperature 23.0 °C | 841 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| 8.00 kJ/m² @Temperature 23.0 °C | 3.81 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 11.5 J/cm² @Temperature 23.0 °C | 54.7 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.550 J/cm² @Temperature 23.0 °C | 2.62 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 0.800 J/cm² @Temperature 23.0 °C | 3.81 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | DAM; ISO 75-1/-2 | ||
| UL RTI, Electrical | 65.0 °C @Thickness 0.810 mm | 149 °F @Thickness 0.0319 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.810 mm | 149 °F @Thickness 0.0319 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 0.810 mm | 149 °F @Thickness 0.0319 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 256 °C | 493 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Filler | Mineral filler | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-IMD40< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Low Warp Resins | DAM | |||
| Mineral Reinforced Resins | DAM | ||||
| Resin Identification | PA66-IMD40 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||