- 密度 [g/cm3]: 1.14
- 缺口冲击强度: 5.0
- 拉伸强度 [MPa]: 55.0
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 55.0 MPa @Temperature 23.0 °C | 7980 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 84.0 MPa @Temperature 23.0 °C | 12200 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 50 % @Temperature 23.0 °C | 50 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| Elongation at Yield | 4.0 % @Temperature 23.0 °C | 4.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 26 % @Temperature 23.0 °C | 26 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.20 GPa @Temperature 23.0 °C | 174 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 3.00 GPa @Temperature 23.0 °C | 435 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C | 2.38 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| 15.0 kJ/m² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 1.80 J/cm² @Temperature 23.0 °C | 8.57 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM | ||
| Descriptive Properties | |||||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | PA66 | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Processing Method | Extrusion | DAM | |||
| Injection Molding | DAM | ||||
| Product Category | Extrusion Resins | DAM | |||
| Unreinforced Resins | DAM | ||||
| RoHS Compliance | Contact Manufacturer | DAM | |||