- 密度 [g/cm3]: 1.14
- 拉伸强度 [MPa]: 65.0
- 热变形温度 [℃]: 221.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0068 cm/cm @Thickness 2.00 mm | 0.0068 in/in @Thickness 0.0787 in | DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 2.00 mm | 0.010 in/in @Thickness 0.0787 in | DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 65.0 MPa @Temperature 23.0 °C | 9430 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 93.0 MPa @Temperature 23.0 °C | 13500 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 14 % @Temperature 23.0 °C | 14 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 18 % @Temperature 23.0 °C | 18 % @Temperature 73.4 °F | DAM; 50mm/min; ISO 527 | |||
| 40 % @Temperature 23.0 °C | 40 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 57 % @Temperature 23.0 °C | 57 % @Temperature 73.4 °F | 50%RH; 50mm/min; ISO 527 | |||
| Elongation at Yield | 4.7 % @Temperature 23.0 °C | 4.7 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 19 % @Temperature 23.0 °C | 19 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.94 GPa @Temperature 23.0 °C | 281 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 3.40 GPa @Temperature 23.0 °C | 493 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature 23.0 °C | 1.90 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 1.00 J/cm² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 262 °C | 504 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 290 °C | 554 °F | DAM; optimum | ||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; Optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Dehumidified Dryer | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Natural Color | ||||
| Forms | Pellets | ||||
| Generic | PA66 | ||||
| Material Status | Preliminary Data | ||||
| Part Marking Code | >PA66< | ISO 11469 | |||
| Processing Method | Injection Molding | ||||
| Product Category | Extrusion Resins | ||||
| Region Available - Global | Yes | ||||
| Resin Identification | PA66 | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Food Applications, Non-specific | ||||