- 吸水率 [%]: 0.85
- 缺口冲击强度: 7.1
- 弯曲模量 [MPa]: 7.70
- 热变形温度 [℃]: 258.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ISO 1183 |
| Water Absorption | 0.85 % @Time 86400 sec | 0.85 % @Time 24.0 hour | ISO 62 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.0040 cm/cm @Thickness 2.00 mm | 0.0040 in/in @Thickness 0.0787 in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 174 MPa | 25200 psi | ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 |
| Tensile Modulus | 7.50 GPa | 1090 ksi | ISO 527 |
| Flexural Strength | 250 MPa | 36300 psi | ISO 178 |
| Flexural Modulus | 7.70 GPa | 1120 ksi | ISO 178 |
| Poissons Ratio | 0.40 | 0.40 | ISO 527 |
| Shear Modulus | 2.68 GPa | 389 ksi | Calculated |
| Izod Impact, Notched (ISO) | 7.10 kJ/m² | 3.38 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 3.90 J/cm² @Temperature -30.0 °C | 18.6 ft-lb/in² @Temperature -22.0 °F | ISO 179 |
| 4.20 J/cm² @Temperature 23.0 °C | 20.0 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |
| Charpy Impact, Notched | 0.980 J/cm² @Temperature -30.0 °C | 4.66 ft-lb/in² @Temperature -22.0 °F | ISO 179 |
| 1.09 J/cm² @Temperature 23.0 °C | 5.19 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 3.00e+15 ohm-cm @Thickness 3.00 mm | 3.00e+15 ohm-cm @Thickness 0.118 in | IEC 60093 |
| Dielectric Strength | 16.0 kV/mm @Thickness 3.00 mm | 406 kV/in @Thickness 0.118 in | IEC 60243 |
| Comparative Tracking Index | 400 - 599 V @Thickness 3.00 mm | 400 - 599 V @Thickness 0.118 in | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 3.50 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 1.94 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359 |
| CTE, linear, Transverse to Flow | 11.0 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 6.11 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359 |
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 |
| Vicat Softening Point | 251 °C @Load 5.10 kg | 484 °F @Load 11.2 lb | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 280 - 310 °C | 536 - 590 °F | |
| Melt Temperature | 285 - 305 °C | 545 - 581 °F | |
| Mold Temperature | 65.0 - 95.0 °C | 149 - 203 °F | |
| Injection Pressure | 55.0 - 140 MPa | 7980 - 20300 psi | |
| Hold Pressure | 55.0 - 140 MPa | 7980 - 20300 psi | |
| Back Pressure | 0.200 - 1.00 MPa | 29.0 - 145 psi | |
| Clamp Pressure | 29.43 - 68.67 MPa | 4268 - 9960 psi | |
| Cushion | 0.300 - 0.640 cm | 0.118 - 0.252 in | |
| Screw Speed | 60 - 120 rpm | 60 - 120 rpm | |