- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 1.2
- 缺口冲击强度: 0.587
- 拉伸强度 [MPa]: 80.0
- 弯曲模量 [MPa]: 3.03
- 热变形温度 [℃]: 235.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | at 24 hours; ASTM D570 |
| Water Absorption at Saturation | 8.5 % | 8.5 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | ASTM D638 |
| Flexural Strength | 107 MPa | 15500 psi | ASTM D790 |
| Flexural Modulus | 3.03 GPa | 440 ksi | ASTM D790 |
| Compressive Strength | 34.5 MPa | 5000 psi | ASTM D695 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.26 | 0.26 | 40 psi, 50 fpm; ASTM D3702 |
| K (wear) Factor | 403 x 10-8 mm³/N-M | 200 x 10-10 in³-min/ft-lb-hr | 40 psi, 50 fpm; ASTM D3702 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz | 3.6 @Frequency 1e+6 Hz | ASTM D150 |
| 4.0 @Frequency 60 Hz | 4.0 @Frequency 60 Hz | ASTM D150 | |
| Dielectric Strength | 11.8 - 15.7 kV/mm | 300 - 400 kV/in | ASTM D149 |
| Dissipation Factor | 0.010 @Frequency 60 Hz | 0.010 @Frequency 60 Hz | ASTM D150 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 81.0 µm/m-°C @Temperature 20.0 °C | 45.0 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Specific Heat Capacity | 1.67 J/g-°C | 0.400 BTU/lb-°F | |
| Melting Point | 255 °C | 491 °F | ASTM D2133 |
| Maximum Service Temperature, Air | 85.0 °C | 185 °F | Long Term; ASTM UL746B |
| 149 °C | 300 °F | Intermittent | |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | |