- 密度 [g/cm3]: 1.5
- 吸水率 [%]: 0.6
- 缺口冲击强度: 1.6
- 断裂伸长率 [%]: 317
- 弯曲强度 [MPa]: 221.0
- 弯曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ASTM D792 |
| Water Absorption | 0.60 % | 0.60 % | 24 hours; ASTM D570 |
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | ASTM D570 |
| Water Absorption at Saturation | 4.7 % | 4.7 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 100 | 100 | ASTM D785 |
| Tensile Strength, Ultimate | 221 MPa | 32100 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 317 MPa | 46000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Compressive Yield Strength | 241 MPa | 35000 psi | at 1% deformation; ASTM D695 |
| Shear Strength | 93.0 MPa | 13500 psi | ASTM D732 |
| Izod Impact, Notched | 1.60 J/cm @Thickness 3.17 mm | 3.00 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 22.0 µm/m-°C @Temperature -40.0 - 82.0 °C | 12.2 µin/in-°F @Temperature -40.0 - 180 °F | |
| Melting Point | 260 °C | 500 °F | ASTM D1525 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C @Thickness 3.17 mm | 491 °F @Thickness 0.125 in | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Oxygen Index | 25 % | 25 % | ASTM D2863 |