- 缺口冲击强度: 0.747
- 弯曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0070 cm/cm @Thickness 3.17 mm | 0.0030 - 0.0070 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 130 MPa | 18900 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 150.0 MPa | 21750 psi | ASTM D790 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm | 1.40 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| V-0 - 5VA @Thickness 3.00 mm | V-0 - 5VA @Thickness 0.118 in | ||