- 密度 [g/cm3]: 1.39
- 缺口冲击强度: 0.801
- 弯曲模量 [MPa]: 8.27
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Density | 1.39 g/cc | 0.0502 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 and ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527-2 |
| 162 MPa | 23500 psi | ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Strength | 220 MPa | 31900 psi | ISO 178 |
| 221 MPa | 32000 psi | ASTM D790 | |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| 8.27 GPa | 1200 ksi | ISO 178 | |
| Izod Impact, Notched | 0.801 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 6.09 kJ/m² | 2.90 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 241 °C | 465 °F | Unannealed; ASTM D648 |
| 241 °C | 466 °F | Unannealed; ASTM D648 | |