- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 0.4
- 缺口冲击强度: 1.7
- 拉伸强度 [MPa]: 210.0
- 断裂伸长率 [%]: 305
- 弯曲模量 [MPa]: 16.5
- 硬度: 122.0
- 热变形温度 [℃]: 250.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 122 | 122 | ASTM D786 |
| Tensile Strength, Yield | 210 MPa | 30500 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Yield Strength | 305 MPa | 44200 psi | ASTM D790 |
| Flexural Modulus | 16.5 GPa | 2390 ksi | ASTM D790 |
| Izod Impact, Notched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 70.0 J/cm @Thickness 3.20 mm | 131 ft-lb/in @Thickness 0.126 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |