- 吸水率 [%]: 0.4
- 缺口冲击强度: 1.57
- 弯曲模量 [MPa]: 16.7
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D792 |
| Water Absorption | 0.40 % @Time 86400 sec | 0.40 % @Time 24.0 hour | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 216 MPa | 31300 psi | ASTM D638 |
| Elongation at Break | 1.8 % | 1.8 % | ASTM D638 |
| Flexural Strength | 324 MPa | 47000 psi | ASTM D790 |
| Flexural Modulus | 16.7 GPa | 2420 ksi | ASTM D790 |
| Izod Impact, Notched | 1.57 J/cm | 2.94 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 310 °C | 536 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |