- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 1.35
- 缺口冲击强度: 1.33
- 拉伸强度 [MPa]: 144.0
- 弯曲模量 [MPa]: 8.3985
- 硬度: 118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | MD; ASTM D955 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength at Break | 143.0 MPa | 20740 psi | ASTM D638 |
| Tensile Strength, Yield | 144.0 MPa | 20880 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 4.200 GPa | 609.1 ksi | ASTM D638 |
| Flexural Strength | 213.9 MPa | 31030 psi | ASTM D790 |
| Flexural Modulus | 8.3985 GPa | 1218.1 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.50 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | |