- 吸水率 [%]: 0.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Filler Content | 60 % | 60 % | ISO 1172 |
| Water Absorption | 0.90 - 1.2 % @Temperature 23.0 °C | 0.90 - 1.2 % @Temperature 73.4 °F | 50% r.h.; ISO 62 |
| Water Absorption at Saturation | 3.9 - 4.4 % @Time 82800 sec | 3.9 - 4.4 % @Time 23.0 hour | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0028 cm/cm | 0.0028 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0067 cm/cm | 0.0067 in/in | ISO 294-4 |
| Spiral Flow | 345 cm | 136 in | Cross Section: 7[mm]x3.5[mm]; AKRO |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 150 MPa | 21800 psi | 5 [mm/min]; ISO 527-1/2 |
| 75.0 MPa @Temperature 160 - 175 °C, Time 1.80e+7 sec | 10900 psi @Temperature 320 - 347 °F, Time 5000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ISO 527-1/2 | |
| 75.0 MPa @Temperature 130 - 150 °C, Time 7.20e+7 sec | 10900 psi @Temperature 266 - 302 °F, Time 20000 hour | 5 [mm/min], 50% Loss of Tensile Strength; ISO 527-1/2 | |
| Elongation at Break | 3.5 % | 3.5 % | 5 [mm/min]; ISO 527-1/2 |
| Tensile Modulus | 15.5 GPa | 2250 ksi | 1[mm/min]; ISO 527-1/2 |
| Charpy Impact Unnotched | 9.50 J/cm² @Temperature 23.0 °C | 45.2 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU |
| Charpy Impact, Notched | 2.50 J/cm² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ISO 11357-1/3 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Nozzle Temperature | 240 - 280 °C | 464 - 536 °F | |
| Zone 1 | 225 - 300 °C | 437 - 572 °F | |
| Zone 2 | 225 - 300 °C | 437 - 572 °F | |
| Zone 3 | 225 - 300 °C | 437 - 572 °F | |
| Zone 4 | 225 - 300 °C | 437 - 572 °F | |
| Melt Temperature | 260 - 300 °C | 500 - 572 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 - 12.0 hour | 4 - 12.0 hour | |
| Injection Pressure | 100 MPa | 14500 psi | |
| Hold Pressure | 75.0 MPa | 10900 psi | |
| Back Pressure | 0.400 - 1.00 MPa | 58.0 - 145 psi | |