- 密度 [g/cm3]: 1.13
- 拉伸强度 [MPa]: 66.0
- 弯曲强度 [MPa]: 76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0410 lb/in³ | Yield Density |
| Thickness | 50.8 microns | 2.00 mil | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 76.0 MPa | 11000 psi | ASTM D882 |
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | ASTM D882 |
| Elongation at Break | 300 % | 300 % | ASTM D882 |
| Tear Strength Test | 30 | 30 | grams/mil; ASTM D1922 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | crystalline melting point; Hot Stage Microscope |
| Shrinkage | <= 1.0 % | <= 1.0 % | 0.5 hr. @ 300°F/149°C; ASTM D1204 |