- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 1.2
- 断裂伸长率 [%]: 270
- 弯曲强度 [MPa]: 160.0
- 弯曲模量 [MPa]: 6.24
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO data |
| Water Absorption | 1.2 % | 1.2 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 7.1 % | 7.1 % | in water; 23°C; ISO data |
| Viscosity Measurement | 50 | 50 | Formic Acid Viscosity; ISO data |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 160 MPa | 23200 psi | ASTM data at 5 mm/min. |
| 161 MPa | 23400 psi | ISO value at 5mm/min. | |
| Elongation at Break | 3.0 % | 3.0 % | Strain at break, ISO, 5 mm/min |
| 3.0 % | 3.0 % | Strain at break, ASTM, 5 mm/min | |
| Flexural Yield Strength | 270 MPa | 39200 psi | ASTM Data |
| Flexural Modulus | 6.24 GPa | 905 ksi | ISO Value |
| 7.31 GPa | 1060 ksi | ASTM Value | |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ASTM Data |
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | |
| HB @Thickness 6.00 mm | HB @Thickness 0.236 in | ||
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |