- 熔体流动速率 [g/10min]: 3.5
- 密度 [g/cm3]: 1.05
- 吸水率 [%]: 0.7
- 拉伸强度 [MPa]: 33.0
- 弯曲强度 [MPa]: 52.0
- 弯曲模量 [MPa]: 0.690
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO R1183 |
| Water Absorption | 0.70 % | 0.70 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 23°C / 50% RH; ISO 62 |
| 5.5 % | 5.5 % | in 23°C water; ISO 62 | |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 235 °C | 3.5 g/10 min @Load 4.76 lb, Temperature 455 °F | after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ISO 868 |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ISO R527 |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | ISO R527 |
| Elongation at Break | >= 250 % | >= 250 % | ISO R527 |
| Elongation at Yield | 7.0 % | 7.0 % | ISO R527 |
| Modulus of Elasticity | 0.800 GPa | 116 ksi | ISO R527 |
| Flexural Strength | 17.5 MPa | 2540 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| Flexural Modulus | 0.690 GPa | 100 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| Charpy Impact, Notched | 4.00 J/cm² | 19.0 ft-lb/in² | After conditioning at 23°C/50%RH; ISO 179/Af |
| 1.20 J/cm² @Temperature -20.0 °C | 5.71 ft-lb/in² @Temperature -4.00 °F | After conditioning at 23°C/50%RH; ISO 179/Af | |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ISO R1218 |
| Flammability, UL94 | HB | HB | |