- 密度 [g/cm3]: 1.41
- 吸水率 [%]: 1.0
- 断裂伸长率 [%]: 290
- 弯曲强度 [MPa]: 185.0
- 弯曲模量 [MPa]: 9.67
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ISO data |
| Water Absorption | 1.0 % | 1.0 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 6.3 % | 6.3 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 185 MPa | 26800 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 3.5 % | 3.5 % | Strain at break, ASTM, 5 mm/min |
| 3.5 % | 3.5 % | Strain at break, ISO, 5 mm/min | |
| Flexural Yield Strength | 290 MPa | 42100 psi | ASTM Data |
| Flexural Modulus | 9.67 GPa | 1400 ksi | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |