- 密度 [g/cm3]: 0.932
- 吸水率 [%]: 1.6
- 缺口冲击强度: 0.48
- 拉伸强度 [MPa]: 78.0
- 弯曲模量 [MPa]: 2.40
- 硬度: 119.0
- 热变形温度 [℃]: 150.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.932 g/cc | 0.0337 lb/in³ | Melt; ISO 1183 | ||
| 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 | |||
| Water Absorption | 1.6 % | 1.6 % | 24 hour; ISO Test | ||
| 9.5 % | 9.5 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | 23°C/50% R.H.; ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Viscosity Measurement | 48 | 48 | Formic Acid | ||
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ASTM Test | ||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Yield | 78.0 MPa | 11300 psi | 50mm/min; ISO 527 | ||
| 79.0 MPa | 11500 psi | 2 in/min; ASTM Test | |||
| 25.0 MPa @Temperature 120 °C | 3630 psi @Temperature 248 °F | ISO Data | |||
| 25.0 MPa @Temperature 120 °C | 3630 psi @Temperature 248 °F | ASTM Test | |||
| 35.0 MPa @Temperature 80.0 °C | 5080 psi @Temperature 176 °F | ASTM Test | |||
| 35.0 MPa @Temperature 80.0 °C | 5080 psi @Temperature 176 °F | ISO Data | |||
| 126 MPa @Temperature -40.0 °C | 18300 psi @Temperature -40.0 °F | ASTM Test | |||
| 126 MPa @Temperature -40.0 °C | 18300 psi @Temperature -40.0 °F | ISO Data | |||
| Elongation at Break | 25 % | 25 % | 50mm/min, Nominal strain; ISO 527 | ||
| 55 % | 55 % | 2 in/min; ASTM Test | |||
| Elongation at Yield | 4.0 % | 4.0 % | 50mm/min; ISO 527 | ||
| 4.0 % | 4.0 % | 2 in/min; ASTM Test | |||
| 36 % @Temperature 120 °C | 36 % @Temperature 248 °F | ISO Data | |||
| 36 % @Temperature 120 °C | 36 % @Temperature 248 °F | ASTM Test | |||
| 42 % @Temperature 80.0 °C | 42 % @Temperature 176 °F | ISO Data | |||
| 42 % @Temperature 80.0 °C | 42 % @Temperature 176 °F | ASTM Test | |||
| Tensile Modulus | 2.70 GPa | 392 ksi | 1mm/min; ISO 527 | ||
| 0.360 GPa @Temperature 120 °C | 52.2 ksi @Temperature 248 °F | ISO Data | |||
| 0.485 GPa @Temperature 80.0 °C | 70.3 ksi @Temperature 176 °F | ISO Data | |||
| Flexural Strength | 85.0 MPa | 12300 psi | ISO Data | ||
| 108 MPa | 15700 psi | ASTM Test | |||
| 17.0 MPa @Temperature 120 °C | 2470 psi @Temperature 248 °F | ASTM Test | |||
| 20.0 MPa @Temperature 93.0 °C | 2900 psi @Temperature 199 °F | ASTM Test | |||
| 30.0 MPa @Temperature 65.0 °C | 4350 psi @Temperature 149 °F | ASTM Test | |||
| 170 MPa @Temperature -40.0 °C | 24700 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 2.40 GPa | 348 ksi | ISO Data | ||
| 2.83 GPa | 410 ksi | ASTM Test | |||
| 0.305 GPa @Temperature 120 °C | 44.2 ksi @Temperature 248 °F | ASTM Test | |||
| 0.350 GPa @Temperature 93.0 °C | 50.8 ksi @Temperature 199 °F | ASTM Test | |||
| 0.500 GPa @Temperature 65.0 °C | 72.5 ksi @Temperature 149 °F | ASTM Test | |||
| Izod Impact, Notched | 0.480 J/cm @Temperature -40.0 °C | 0.899 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 0.580 J/cm @Thickness 3.17 mm | 1.09 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| 5.10 J/cm² @Temperature -30.0 °C | 24.3 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 0.350 J/cm² | 1.67 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz | 3.3 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.5 @Frequency 100 Hz | 3.5 @Frequency 100 Hz | IEC 60250 | |||
| 4.1 @Frequency 1.00e+6 Hz | 4.1 @Frequency 1.00e+6 Hz | ASTM Data | |||
| 4.3 @Frequency 1e+9 Hz | 4.3 @Frequency 1e+9 Hz | ASTM Data | |||
| Dielectric Strength | 37.0 kV/mm | 940 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.010 @Frequency 1e+9 Hz | 0.010 @Frequency 1e+9 Hz | ASTM Data | ||
| 0.010 @Frequency 1.00e+6 Hz | 0.010 @Frequency 1.00e+6 Hz | ASTM Data | |||
| 0.010 @Frequency 100 Hz | 0.010 @Frequency 100 Hz | IEC 60250 | |||
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 83.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 46.1 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Specific Heat Capacity | 3.728 J/g-°C | 0.8910 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.264 W/m-K | 1.83 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75 | ||
| 178 °C | 352 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75 | ||
| 65.0 °C | 149 °F | ASTM Test | |||
| Flammability, UL94 | V-2 @Thickness 0.700 mm | V-2 @Thickness 0.0276 in | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | Injection molding | ||
| Mold Temperature | 80.0 °C | 176 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||