- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 缺口冲击强度: 0.55
- 拉伸强度 [MPa]: 85.0
- 弯曲模量 [MPa]: 2.65
- 硬度: 119.0
- 热变形温度 [℃]: 178.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.6 % | 1.6 % | 24 hour; ISO Test | ||
| 9.5 % | 9.5 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | 23°C/50% R.H.; ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Viscosity Measurement | 48 | 48 | Formic Acid | ||
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ASTM Test | ||
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | 50mm/min; ISO 527 | ||
| 85.0 MPa | 12300 psi | 2 in/min; ASTM Test | |||
| Elongation at Break | 25 % | 25 % | 50mm/min, Nominal strain; ISO 527 | ||
| 50 % | 50 % | 2 in/min; ASTM Test | |||
| Elongation at Yield | 4.0 % | 4.0 % | 50mm/min; ISO 527 | ||
| 4.0 % | 4.0 % | 2 in/min; ASTM Test | |||
| Tensile Modulus | 3.10 GPa | 450 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO Data | ||
| 108 MPa | 15700 psi | ASTM Test | |||
| Flexural Modulus | 2.65 GPa | 384 ksi | ISO Data | ||
| 2.83 GPa | 410 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.550 J/cm @Thickness 3.17 mm | 1.03 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 5.50 kJ/m² | 2.62 ft-lb/in² | ISO Test | ||
| 4.00 kJ/m² @Temperature -40.0 °C | 1.90 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 83.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 46.1 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 178 °C | 352 °F | ASTM Test | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75 | ||
| 65.0 °C | 149 °F | ASTM Test | |||
| Flammability, UL94 | V-2 @Thickness 0.700 mm | V-2 @Thickness 0.0276 in | |||
| V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | ||||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||