- 密度 [g/cm3]: 1.2784
- 吸水率 [%]: 0.9
- 弯曲强度 [MPa]: 145.0
- 弯曲模量 [MPa]: 6.56
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.2784 g/cc | 0.046185 lb/in³ | Melt; ISO 1183 | ||
| 1.49 g/cc | 0.0538 lb/in³ | dry; ISO 1183 | |||
| Water Absorption | 0.90 % | 0.90 % | 24 hour; ISO Test | ||
| 5.2 % | 5.2 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Viscosity Measurement | 50 | 50 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 145 MPa | 21000 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 6.0 % | 6.0 % | 5mm/min; ISO 527 | ||
| 6.0 % | 6.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 7.49 GPa | 1090 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 212 MPa | 30700 psi | ASTM Test | ||
| 410 MPa @Temperature -40.0 °C | 59500 psi @Temperature -40.0 °F | ASTM Test | |||
| Flexural Modulus | 6.56 GPa | 951 ksi | ASTM Test | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Comparative Tracking Index | 500 V | 500 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 2.522 J/g-°C | 0.6028 BTU/lb-°F | Melt | ||
| Thermal Conductivity | 0.329 W/m-K | 2.28 BTU-in/hr-ft²-°F | Melt | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||