- 密度 [g/cm3]: 1.55
- 吸水率 [%]: 4.8
- 缺口冲击强度: 12.0
- 弯曲强度 [MPa]: 203.0
- 弯曲模量 [MPa]: 14.5
- 热变形温度 [℃]: 218.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 | ||
| Water Absorption | 4.8 % | 4.8 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 23°C/50% R.H.; ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 203 MPa | 29400 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.1 % | 2.1 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 15.0 GPa | 2180 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 14.5 GPa | 2100 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO Test | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK00564 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||