- 密度 [g/cm3]: 1.74
- 缺口冲击强度: 1.55
- 弯曲强度 [MPa]: 245.0
- 弯曲模量 [MPa]: 17.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 207 MPa | 30000 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 245 MPa | 35500 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.0 % | 2.0 % | 5mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 22.4 GPa | 3250 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 355 MPa | 51500 psi | ISO Data | ||
| 378 MPa | 54800 psi | ASTM Test | |||
| Flexural Modulus | 17.3 GPa | 2510 ksi | ASTM Test | ||
| 18.0 GPa | 2610 ksi | ISO Data | |||
| Izod Impact, Notched | 1.55 J/cm @Thickness 3.17 mm | 2.90 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Unnotched | 13.88 J/cm | 26.00 ft-lb/in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 12.5 kJ/m² | 5.95 ft-lb/in² | ISO Test | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | ASTM Test | ||
| 214 °C | 417 °F | ISO 75 | |||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||