- 熔体流动速率 [g/10min]: 121.0
- 密度 [g/cm3]: 1.1
- 吸水率 [%]: 8.5
- 缺口冲击强度: 5.5
- 拉伸强度 [MPa]: 70.0
- 弯曲模量 [MPa]: 2.30
- 热变形温度 [℃]: 150.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 | ||
| Water Absorption | 8.5 - 9.5 % | 8.5 - 9.5 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.1 - 2.9 % | 2.1 - 2.9 % | 23°C; 50% RH; ISO 62 | ||
| Linear Mold Shrinkage | 0.0065 cm/cm | 0.0065 in/in | restricted | ||
| Melt Flow | 121 g/10 min @Load 5.00 kg, Temperature 275 °C | 121 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 3.5 % | 3.5 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 2.80 GPa | 406 ksi | ISO 527-1/-2 | ||
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.50 kJ/m² @Temperature -30.0 °C | 2.62 ft-lb/in² @Temperature -22.0 °F | ISO 180/A | ||
| 15.0 kJ/m² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | ISO 180/A | |||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.00 J/cm² @Temperature 23.0 °C | 4.76 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 1.00 Hz | 3.5 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.024 @Frequency 1.00e+6 Hz | 0.024 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.700 - 1.00 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.389 - 0.556 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |||
| Thermal Conductivity | 0.320 W/m-K | 2.22 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 160 °C | 320 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||