- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 5.0
- 拉伸强度 [MPa]: 170.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |||
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 | ||
| Water Absorption | 5.0 - 6.0 % | 5.0 - 6.0 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.1 - 1.5 % | 1.1 - 1.5 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 130 | 130 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0039 cm/cm | 0.0039 in/in | restricted | ||
| Linear Mold Shrinkage, Flow | 0.0045 cm/cm | 0.0045 in/in | ISO 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 170 MPa | 24700 psi | 50 mm/min; ISO 527-1/-2 | ||
| Tensile Creep Modulus, 1000 hours | 6500 MPa @Strain <=0.500 % | 943000 psi @Strain <=0.500 % | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Constant | 4.5 @Frequency 1.00 Hz | 4.5 @Frequency 1.00 Hz | IEC 60250 | ||
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.040 @Frequency 1.00e+6 Hz | 0.040 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 295 °C | 563 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20000hr | ||
| 160 °C | 320 °F | for 50% loss of tensile strength after 5000hr | |||
| 270 °C | 518 °F | ||||
| Decomposition Temperature | >= 350 °C | >= 662 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Zone 1 | 300 °C | 572 °F | Feed Zone | ||
| Zone 2 | 310 °C | 590 °F | Compression | ||
| Zone 3 | 320 °C | 608 °F | Metering-zone | ||
| Zone 4 | 320 °C | 608 °F | Nozzle | ||
| Melt Temperature | 310 - 330 °C | 590 - 626 °F | Injection-molding/Extrusion | ||
| 320 °C | 608 °F | Optimal | |||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | Injection-molding | ||
| 100 °C | 212 °F | Optimal | |||
| Drying Temperature | 110 °C | 230 °F | |||
| Dry Time | 8 hour | 8 hour | |||
| Moisture Content | <= 0.030 % | <= 0.030 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Color | BK 00564 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >470°C | ASTM D1929 | |||