- 密度 [g/cm3]: 1.37
- 缺口冲击强度: 23.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | ||
| Moisture Absorption at Equilibrium | >= 0.80 % | >= 0.80 % | 50% RH; ISO 62 | ||
| >= 4.5 % | >= 4.5 % | Saturation; ISO 62 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 165 MPa @Temperature 23.0 °C | 23900 psi @Temperature 73.4 °F | ISO 527 | ||
| 249 MPa @Temperature -40.0 °C | 36100 psi @Temperature -40.0 °F | ISO 527 | |||
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 | ||
| Modulus of Elasticity | 9.30 GPa | 1350 ksi | ISO 527-1/-2 | ||
| Izod Impact, Notched (ISO) | 23.0 kJ/m² @Temperature 23.0 °C | 10.9 ft-lb/in² @Temperature 73.4 °F | ISO 180/A | ||
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -30.0 °C | 42.8 ft-lb/in² @Temperature -22.0 °F | ISO 179 | ||
| 9.50 J/cm² @Temperature 23.0 °C | 45.2 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |||
| Charpy Impact, Notched | 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 179 | ||
| 1.90 J/cm² @Temperature 23.0 °C | 9.04 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 4.3 @Frequency 1.00 Hz | 4.3 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.030 @Frequency 1.00e+6 Hz | 0.030 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.250 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.139 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 0.550 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.306 µin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | |||
| Melting Point | 295 °C | 563 °F | DIN 53765 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 350 °C | >= 662 °F | |||
| UL RTI, Electrical | 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical with Impact | 110 °C @Thickness 1.50 mm | 230 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical without Impact | 140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | 746B | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 300 °C | 572 °F | Feed Zone | ||
| Zone 2 | 310 °C | 590 °F | Compression | ||
| Zone 3 | 320 °C | 608 °F | Metering-zone | ||
| Zone 4 | 320 °C | 608 °F | Nozzle | ||
| Descriptive Properties | |||||
| Color | BK 00564 | ||||
| Commercial Status | North America | ||||
| Peripheral Screw Speed | <0.3 m/s | ||||