- 密度 [g/cm3]: 1.3
- 缺口冲击强度: 50.0
- 拉伸强度 [MPa]: 25.0
- 弯曲模量 [MPa]: 0.305
- 硬度: 119.0
- 热变形温度 [℃]: 178.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 24 hour; ASTM D570 | ||
| 2.7 % | 2.7 % | 50% RH; ASTM D570 | |||
| 9.5 % | 9.5 % | Saturation; ASTM D570 | |||
| Linear Mold Shrinkage | 0.0305 cm/cm | 0.0305 in/in | 1/8" Bar | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ASTM D785 | ||
| Tensile Strength at Break | 75.0 MPa @Temperature -40.0 °C | 10900 psi @Temperature -40.0 °F | ASTM D638 | ||
| Tensile Strength, Yield | 25.0 MPa @Temperature 121 °C | 3630 psi @Temperature 250 °F | ASTM D638 | ||
| 35.0 MPa @Temperature 80.0 °C | 5080 psi @Temperature 176 °F | ASTM D638 | |||
| 79.0 MPa @Temperature 23.0 °C | 11500 psi @Temperature 73.4 °F | ASTM D638 | |||
| 125 MPa @Temperature -40.0 °C | 18100 psi @Temperature -40.0 °F | ASTM D638 | |||
| Elongation at Break | 55 % | 55 % | ASTM D638 | ||
| Elongation at Yield | 4.0 % @Temperature 23.0 °C | 4.0 % @Temperature 73.4 °F | |||
| 36 % @Temperature 121 °C | 36 % @Temperature 250 °F | ||||
| 42 % @Temperature 80.0 °C | 42 % @Temperature 176 °F | ||||
| Flexural Strength | 20.0 MPa @Temperature 250 °C | 2900 psi @Temperature 482 °F | ASTM D790 | ||
| 20.0 MPa @Temperature 194 °C | 2900 psi @Temperature 381 °F | ASTM D790 | |||
| 30.0 MPa @Temperature 149 °C | 4350 psi @Temperature 300 °F | ASTM D790 | |||
| 110 MPa @Temperature 23.0 °C | 16000 psi @Temperature 73.4 °F | ASTM D790 | |||
| 170 MPa @Temperature -40.0 °C | 24700 psi @Temperature -40.0 °F | ASTM D790 | |||
| Flexural Modulus | 0.305 GPa @Temperature 121 °C | 44.2 ksi @Temperature 250 °F | ASTM D790 | ||
| 0.350 GPa @Temperature 90.0 °C | 50.8 ksi @Temperature 194 °F | ASTM D790 | |||
| 0.500 GPa @Temperature 65.0 °C | 72.5 ksi @Temperature 149 °F | ASTM D790 | |||
| 2.83 GPa @Temperature 23.0 °C | 410 ksi @Temperature 73.4 °F | ASTM D790 | |||
| 3.01 GPa @Temperature -40.0 °C | 437 ksi @Temperature -40.0 °F | ASTM D790 | |||
| Izod Impact, Notched (ISO) | 50.0 kJ/m² @Temperature -40.0 °C | 23.8 ft-lb/in² @Temperature -40.0 °F | ASTM D256 | ||
| 60.0 kJ/m² @Temperature 23.0 °C | 28.6 ft-lb/in² @Temperature 73.4 °F | ASTM D256 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 0.830 µm/m-°C | 0.461 µin/in-°F | ASTM E831 | ||
| Melting Point | 220 °C | 428 °F | ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 178 °C | 352 °F | ASTM D684 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D684 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 240 - 285 °C | 464 - 545 °F | |||
| Mold Temperature | 65.0 - 80.0 °C | 149 - 176 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.15 % | <= 0.15 % | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Commercial Status | North America | ||||