- 密度 [g/cm3]: 1.21
- 缺口冲击强度: 5.4
- 弯曲模量 [MPa]: 4.39
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 | ||
| Elongation at Break | 3.5 % | 3.5 % | ISO 527 | ||
| Flexural Modulus | 4.39 GPa | 637 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.40 kJ/m² @Temperature -40.0 °C | 2.57 ft-lb/in² @Temperature -40.0 °F | ISO 180 | ||
| 17.0 kJ/m² @Temperature 23.0 °C | 8.09 ft-lb/in² @Temperature 73.4 °F | ISO 180 | |||
| Charpy Impact, Notched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75 | ||
| UL RTI, Electrical | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | 746B | ||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | 746B | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |||
| Processing Properties | Metric | English | Comments | ||
| Zone 1 | 245 - 275 °C | 473 - 527 °F | Rear Zone | ||
| Zone 2 | 260 - 285 °C | 500 - 545 °F | Center Zone | ||
| Zone 3 | 270 - 295 °C | 518 - 563 °F | Front Zone | ||
| Zone 4 | 270 - 295 °C | 518 - 563 °F | Nozzle | ||
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | |||
| Mold Temperature | 80.0 - 95.0 °C | 176 - 203 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.080 % | <= 0.080 % | |||
| Descriptive Properties | |||||
| Commercial Status | North America | ||||