- 密度 [g/cm3]: 1.8
- 弯曲模量 [MPa]: 18.7
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | |||
| Filler Content | 47 % | 47 % | by volume | ||
| Thickness | 500 microns | 19.7 mil | laminate layer thickness | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 390 MPa | 56600 psi | transverse; ISO 527-4/5 | ||
| 404 MPa | 58600 psi | longitudinal; ISO 527-4/5 | |||
| Elongation at Break | 2.2 % | 2.2 % | transverse; ISO 527-4/5 | ||
| 2.2 % | 2.2 % | longitudinal; ISO 527-4/5 | |||
| Tensile Modulus | 21.5 GPa | 3120 ksi | transverse; ISO 527-4/5 | ||
| 22.4 GPa | 3250 ksi | longitudinal; ISO 527-4/5 | |||
| Flexural Strength | 585 MPa | 84800 psi | transverse; ISO 178 | ||
| 620 MPa | 89900 psi | longitudinal; ISO 178 | |||
| Flexural Modulus | 18.7 GPa | 2710 ksi | transverse; ISO 178 | ||
| 19.2 GPa | 2780 ksi | longitudinal; ISO 178 | |||
| Poissons Ratio | 0.17 | 0.17 | transverse; ISO 527-4/5 | ||
| 0.17 | 0.17 | longitudinal; ISO 527-4/5 | |||
| Charpy Impact Unnotched | 14.5 J/cm² | 69.0 ft-lb/in² | longitudinal; ISO 179/1eU | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 15.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 8.33 µin/in-°F @Temperature 73.4 - 176 °F | transverse; ASTM E831 | ||
| 15.0 µm/m-°C @Temperature 23.0 - 80.0 °C | 8.33 µin/in-°F @Temperature 73.4 - 176 °F | longitudinal; ASTM E831 | |||
| 19.0 µm/m-°C @Temperature -30.0 - 23.0 °C | 10.6 µin/in-°F @Temperature -22.0 - 73.4 °F | transverse; ASTM E831 | |||
| 19.0 µm/m-°C @Temperature -30.0 - 23.0 °C | 10.6 µin/in-°F @Temperature -22.0 - 73.4 °F | longitudinal; ASTM E831 | |||
| Melting Point | 220 °C | 428 °F | DSC 3146 | ||
| Maximum Service Temperature, Air | 120 °C @Time 7.20e+7 sec | 248 °F @Time 20000 hour | Relative Temperature Index; IEC 216/1 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1/2 | ||
| Minimum Service Temperature, Air | -30.0 °C | -22.0 °F | |||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | DSC 3146 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 240 - 260 °C | 464 - 500 °F | |||
| Descriptive Properties | |||||
| Reinforcement | Area weight | 600 g/m² | |||
| Fabric | twill | ||||
| Fibers | roving glass | ||||
| Weight Rate | 50% longitudinal and transverse | ||||
| Yarn | 1200 tex longitudinal and transverse | ||||