- 密度 [g/cm3]: 1.17
- 断裂伸长率 [%]: 83.0
- 弯曲强度 [MPa]: 69.0
- 弯曲模量 [MPa]: 3.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 69.0 MPa | 10000 psi | ASTM D638 |
| Elongation at Break | 15 % | 15 % | ASTM D638 |
| Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ASTM D790 |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | >= 600 V | >= 600 V | CTI, V |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 215 °C | 419 °F | ASTM D789 |
| Flammability, UL94 | V-0 | V-0 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 252 °C | 486 °F | |