- 密度 [g/cm3]: 1.07
- 吸水率 [%]: 1.5
- 缺口冲击强度: 9.6
- 弯曲强度 [MPa]: 48.3
- 弯曲模量 [MPa]: 1.60
- 硬度: 110.0
- 热变形温度 [℃]: 171.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | ASTM D792 |
| Water Absorption | 1.5 % | 1.5 % | 24 hour immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 75 | 75 | ASTM D785 |
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Ultimate | 48.3 MPa | 7010 psi | ASTM D638 |
| Elongation at Break | 70 % | 70 % | ASTM D638 |
| Flexural Strength | 67.0 MPa | 9720 psi | ASTM D790 |
| Flexural Modulus | 1.60 GPa | 232 ksi | ASTM D790 |
| Compressive Yield Strength | 45.0 MPa | 6530 psi | ASTM D695 |
| Izod Impact, Notched | 9.60 J/cm | 18.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 210 °C | 410 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 171 °C | 340 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |