- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 7.0
- 热变形温度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 | ||
| Water Absorption | 7.0 % | 7.0 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | Humidity Absorption; Sim. to ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 | ||
| Elongation at Break | 3.5 % | 3.5 % | ISO 527-1/-2 | ||
| Tensile Modulus | 7.50 GPa | 1090 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature -30.0 °C | 26.2 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 6.00 J/cm² @Temperature 23.0 °C | 28.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.350 J/cm² @Temperature -30.0 °C | 1.67 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.600 J/cm² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature 20.0 °C | 13.9 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 105 µm/m-°C @Temperature 20.0 °C | 58.3 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 0.710 mm | HB @Thickness 0.0280 in | IEC 60695-11-10 | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | |||
| Descriptive Properties | |||||
| Injection Molding | Yes | ||||
| Lubricants | Yes | ||||
| Release agent | Yes | ||||
| With fillers | Yes | ||||