- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 6.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.8 % | 6.8 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | Humidity Absorption; Sim. to ISO 62 | ||
| High Load Melt Index | 48 g/10 min @Load 21.6 kg, Temperature 275 °C | 48 g/10 min @Load 47.6 lb, Temperature 527 °F | Calculated from Volume Flow Rate of 40 cm3/10min.; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 105 MPa | 15200 psi | ISO 527-1/-2 | ||
| Elongation at Break | 5.0 % | 5.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C | 7.14 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 2.50 J/cm² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1/-2 | ||
| Descriptive Properties | |||||
| Blow Molding | Yes | ||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| High Impact or Impact Modified | Yes | ||||
| RSV Formic Acid | 4 g/100ml | ISO 307 | |||
| With Fillers | Yes | ||||