- 密度 [g/cm3]: 1.12
- 缺口冲击强度: 30.0
- 弯曲强度 [MPa]: 47.0
- 弯曲模量 [MPa]: 1.712
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 74 | 74 | ISO 868 |
| Tensile Strength, Ultimate | 47.0 MPa | 6820 psi | ISO 527 |
| Elongation at Break | 270 % | 270 % | ISO 527 |
| Modulus of Elasticity | 1.512 GPa | 219.3 ksi | ISO 527 |
| Flexural Modulus | 1.712 GPa | 248.3 ksi | ISO 178 |
| Shear Modulus | 0.700 GPa | 102 ksi | torsional |
| Izod Impact, Notched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | ISO 180, Ductile break |
| 9.00 kJ/m² @Temperature -40.0 °C | 4.28 ft-lb/in² @Temperature -40.0 °F | Brittle break; ISO 180 | |
| Charpy Impact, Notched | 2.20 J/cm² | 10.5 ft-lb/in² | DIN 53453, Ductile break |
| 1.40 J/cm² @Temperature -40.0 °C | 6.66 ft-lb/in² @Temperature -40.0 °F | Brittle break; DIN 53453 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 213 °C | 415 °F | DSC |