- 密度 [g/cm3]: 1.51
- 吸水率 [%]: 1.5
- 成型收缩率 [%]: 0.001
- 缺口冲击强度: 1.85
- 弯曲模量 [MPa]: 7.00
- 热变形温度 [℃]: 221.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 45 % | 45 % | DAM | ||
| Water Absorption | 1.5 % @Temperature 23.0 °C | 1.5 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 4.9 % @Temperature 23.0 °C | 4.9 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage | 0.0010 cm/cm @Thickness 1.60 mm | 0.0010 in/in @Thickness 0.0630 in | Flow; DAM | ||
| 0.0020 cm/cm @Thickness 3.20 mm | 0.0020 in/in @Thickness 0.126 in | Flow; DAM | |||
| 0.0090 cm/cm @Thickness 3.20 mm | 0.0090 in/in @Thickness 0.126 in | Transverse; DAM | |||
| 0.010 cm/cm @Thickness 1.60 mm | 0.010 in/in @Thickness 0.0630 in | Transverse; DAM | |||
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm @Thickness 2.00 mm | 0.0015 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 160 MPa @Temperature 23.0 °C | 23200 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 230 MPa @Temperature 23.0 °C | 33400 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Strength | 145 MPa @Temperature 23.0 °C | 21000 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | ||
| 214 MPa @Temperature 23.0 °C | 31000 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Tensile Stress | 11.61 MPa @Strain 0.220 %, Temperature 120 °C | 1684 psi @Strain 0.220 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | ||
| 14.01 MPa @Strain 0.230 %, Temperature 150 °C | 2032 psi @Strain 0.230 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 14.03 MPa @Strain 0.270 %, Temperature 120 °C | 2035 psi @Strain 0.270 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 15.49 MPa @Strain 0.320 %, Temperature 150 °C | 2247 psi @Strain 0.320 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 17.77 MPa @Strain 0.270 %, Temperature 120 °C | 2577 psi @Strain 0.270 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 20.22 MPa @Strain 0.250 %, Temperature 60.0 °C | 2933 psi @Strain 0.250 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 20.97 MPa @Strain 0.370 %, Temperature 150 °C | 3041 psi @Strain 0.370 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 21.92 MPa @Strain 0.260 %, Temperature 90.0 °C | 3179 psi @Strain 0.260 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 21.99 MPa @Strain 0.440 %, Temperature 120 °C | 3189 psi @Strain 0.440 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 22.4 MPa @Strain 0.510 %, Temperature 150 °C | 3250 psi @Strain 0.510 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.5 MPa @Strain 0.330 %, Temperature 40.0 °C | 4130 psi @Strain 0.330 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.65 MPa @Strain 0.460 %, Temperature 120 °C | 4155 psi @Strain 0.460 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 29.31 MPa @Strain 0.750 %, Temperature 150 °C | 4251 psi @Strain 0.750 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 30.11 MPa @Strain 0.290 %, Temperature 60.0 °C | 4367 psi @Strain 0.290 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 30.65 MPa @Strain 0.670 %, Temperature 120 °C | 4445 psi @Strain 0.670 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 31.34 MPa @Strain 0.600 %, Temperature 150 °C | 4545 psi @Strain 0.600 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 31.6 MPa @Strain 0.410 %, Temperature 60.0 °C | 4580 psi @Strain 0.410 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.86 MPa @Strain 1.06 %, Temperature 150 °C | 5201 psi @Strain 1.06 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 36.07 MPa @Strain 0.460 %, Temperature 90.0 °C | 5232 psi @Strain 0.460 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 38.69 MPa @Strain 0.390 %, Temperature 23.0 °C | 5612 psi @Strain 0.390 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 38.97 MPa @Strain 0.940 %, Temperature 120 °C | 5652 psi @Strain 0.940 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 40.61 MPa @Strain 0.720 %, Temperature 120 °C | 5890 psi @Strain 0.720 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 41.31 MPa @Strain 0.500 %, Temperature 40.0 °C | 5992 psi @Strain 0.500 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 41.49 MPa @Strain 1.39 %, Temperature 150 °C | 6018 psi @Strain 1.39 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 41.63 MPa @Strain 0.900 %, Temperature 150 °C | 6038 psi @Strain 0.900 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 43.63 MPa @Strain 0.610 %, Temperature 60.0 °C | 6328 psi @Strain 0.610 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 46.51 MPa @Strain 1.79 %, Temperature 150 °C | 6746 psi @Strain 1.79 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 46.59 MPa @Strain 1.27 %, Temperature 120 °C | 6757 psi @Strain 1.27 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.51 MPa @Strain 0.480 %, Temperature 60.0 °C | 7036 psi @Strain 0.480 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 50.81 MPa @Strain 2.21 %, Temperature 150 °C | 7369 psi @Strain 2.21 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 50.92 MPa @Strain 1.26 %, Temperature 150 °C | 7385 psi @Strain 1.26 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 51.05 MPa @Strain 0.700 %, Temperature 90.0 °C | 7404 psi @Strain 0.700 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 52.25 MPa @Strain 1.03 %, Temperature 120 °C | 7578 psi @Strain 1.03 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 53.46 MPa @Strain 1.63 %, Temperature 120 °C | 7754 psi @Strain 1.63 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 54.51 MPa @Strain 2.65 %, Temperature 150 °C | 7906 psi @Strain 2.65 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 54.53 MPa @Strain 0.710 %, Temperature 40.0 °C | 7909 psi @Strain 0.710 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 54.69 MPa @Strain 0.580 %, Temperature 23.0 °C | 7932 psi @Strain 0.580 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 55.59 MPa @Strain 0.840 %, Temperature 60.0 °C | 8063 psi @Strain 0.840 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 57.93 MPa @Strain 3.13 %, Temperature 150 °C | 8402 psi @Strain 3.13 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 59.02 MPa @Strain 1.69 %, Temperature 150 °C | 8560 psi @Strain 1.69 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 59.59 MPa @Strain 2.04 %, Temperature 120 °C | 8643 psi @Strain 2.04 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 60.84 MPa @Strain 3.62 %, Temperature 150 °C | 8824 psi @Strain 3.62 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 62.6 MPa @Strain 1.41 %, Temperature 120 °C | 9080 psi @Strain 1.41 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 63.32 MPa @Strain 4.16 %, Temperature 150 °C | 9184 psi @Strain 4.16 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 63.92 MPa @Strain 4.75 %, Temperature 150 °C | 9271 psi @Strain 4.75 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 64.66 MPa @Strain 2.46 %, Temperature 120 °C | 9378 psi @Strain 2.46 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 65.14 MPa @Strain 0.990 %, Temperature 90.0 °C | 9448 psi @Strain 0.990 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 65.87 MPa @Strain 2.19 %, Temperature 150 °C | 9554 psi @Strain 2.19 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 67.09 MPa @Strain 1.12 %, Temperature 60.0 °C | 9731 psi @Strain 1.12 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 67.34 MPa @Strain 0.940 %, Temperature 40.0 °C | 9767 psi @Strain 0.940 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 67.83 MPa @Strain 0.710 %, Temperature 60.0 °C | 9838 psi @Strain 0.710 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 68.47 MPa @Strain 2.84 %, Temperature 120 °C | 9931 psi @Strain 2.84 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 70.89 MPa @Strain 0.800 %, Temperature 23.0 °C | 10280 psi @Strain 0.800 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 71.73 MPa @Strain 2.69 %, Temperature 150 °C | 10400 psi @Strain 2.69 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 71.74 MPa @Strain 1.82 %, Temperature 120 °C | 10410 psi @Strain 1.82 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 71.86 MPa @Strain 3.22 %, Temperature 120 °C | 10420 psi @Strain 3.22 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 74.89 MPa @Strain 3.62 %, Temperature 120 °C | 10860 psi @Strain 3.62 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 76.93 MPa @Strain 3.27 %, Temperature 150 °C | 11160 psi @Strain 3.27 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 77.47 MPa @Strain 4.01 %, Temperature 120 °C | 11240 psi @Strain 4.01 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 77.58 MPa @Strain 1.44 %, Temperature 60.0 °C | 11250 psi @Strain 1.44 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 78.16 MPa @Strain 1.31 %, Temperature 90.0 °C | 11340 psi @Strain 1.31 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 79.46 MPa @Strain 1.21 %, Temperature 40.0 °C | 11520 psi @Strain 1.21 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 79.61 MPa @Strain 4.47 %, Temperature 120 °C | 11550 psi @Strain 4.47 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 79.69 MPa @Strain 2.31 %, Temperature 120 °C | 11560 psi @Strain 2.31 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 80.63 MPa @Strain 4.96 %, Temperature 120 °C | 11690 psi @Strain 4.96 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 80.67 MPa @Strain 0.630 %, Temperature 0.000 °C | 11700 psi @Strain 0.630 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 81.3 MPa @Strain 3.86 %, Temperature 150 °C | 11800 psi @Strain 3.86 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 83.7 MPa @Strain 0.660 %, Temperature 40.0 °C | 12100 psi @Strain 0.660 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 85.08 MPa @Strain 4.50 %, Temperature 150 °C | 12340 psi @Strain 4.50 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 85.1 MPa @Strain 0.950 %, Temperature 60.0 °C | 12300 psi @Strain 0.950 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 86.36 MPa @Strain 1.05 %, Temperature 23.0 °C | 12530 psi @Strain 1.05 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 86.69 MPa @Strain 2.80 %, Temperature 120 °C | 12570 psi @Strain 2.80 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 86.92 MPa @Strain 1.79 %, Temperature 60.0 °C | 12610 psi @Strain 1.79 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 88.33 MPa @Strain 5.15 %, Temperature 150 °C | 12810 psi @Strain 5.15 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 89.66 MPa @Strain 1.71 %, Temperature 90.0 °C | 13000 psi @Strain 1.71 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 90.23 MPa @Strain 0.630 %, Temperature -20.0 °C | 13090 psi @Strain 0.630 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 90.64 MPa @Strain 1.51 %, Temperature 40.0 °C | 13150 psi @Strain 1.51 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 90.85 MPa @Strain 5.85 %, Temperature 150 °C | 13180 psi @Strain 5.85 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 91.62 MPa @Strain 6.65 %, Temperature 150 °C | 13290 psi @Strain 6.65 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 92.72 MPa @Strain 3.33 %, Temperature 120 °C | 13450 psi @Strain 3.33 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 95.19 MPa @Strain 2.18 %, Temperature 60.0 °C | 13810 psi @Strain 2.18 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 97.6 MPa @Strain 0.790 %, Temperature 0.000 °C | 14200 psi @Strain 0.790 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 97.95 MPa @Strain 3.91 %, Temperature 120 °C | 14210 psi @Strain 3.91 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 100 MPa @Strain 2.12 %, Temperature 90.0 °C | 14500 psi @Strain 2.12 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 100.59 MPa @Strain 1.33 %, Temperature 23.0 °C | 14589 psi @Strain 1.33 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 100.66 MPa @Strain 1.84 %, Temperature 40.0 °C | 14600 psi @Strain 1.84 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 101.45 MPa @Strain 1.23 %, Temperature 60.0 °C | 14714 psi @Strain 1.23 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 102.3 MPa @Strain 2.60 %, Temperature 60.0 °C | 14840 psi @Strain 2.60 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 102.31 MPa @Strain 4.56 %, Temperature 120 °C | 14839 psi @Strain 4.56 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 103.57 MPa @Strain 0.850 %, Temperature 40.0 °C | 15022 psi @Strain 0.850 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 105.95 MPa @Strain 5.19 %, Temperature 120 °C | 15367 psi @Strain 5.19 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 108.46 MPa @Strain 3.04 %, Temperature 60.0 °C | 15731 psi @Strain 3.04 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 108.73 MPa @Strain 5.89 %, Temperature 120 °C | 15770 psi @Strain 5.89 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 109 MPa @Strain 0.840 %, Temperature 23.0 °C | 15800 psi @Strain 0.840 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 109.12 MPa @Strain 2.64 %, Temperature 90.0 °C | 15827 psi @Strain 2.64 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 109.72 MPa @Strain 2.20 %, Temperature 40.0 °C | 15914 psi @Strain 2.20 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 109.88 MPa @Strain 6.70 %, Temperature 120 °C | 15937 psi @Strain 6.70 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 109.93 MPa @Strain 0.780 %, Temperature -20.0 °C | 15944 psi @Strain 0.780 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 113.54 MPa @Strain 3.54 %, Temperature 60.0 °C | 16468 psi @Strain 3.54 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 113.75 MPa @Strain 1.66 %, Temperature 23.0 °C | 16498 psi @Strain 1.66 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 114.46 MPa @Strain 0.970 %, Temperature 0.000 °C | 16601 psi @Strain 0.970 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 116.96 MPa @Strain 3.19 %, Temperature 90.0 °C | 16964 psi @Strain 3.19 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 117.07 MPa @Strain 1.57 %, Temperature 60.0 °C | 16980 psi @Strain 1.57 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 117.44 MPa @Strain 4.11 %, Temperature 60.0 °C | 17033 psi @Strain 4.11 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 117.51 MPa @Strain 4.67 %, Temperature 60.0 °C | 17043 psi @Strain 4.67 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 117.75 MPa @Strain 2.60 %, Temperature 40.0 °C | 17078 psi @Strain 2.60 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 123.1 MPa @Strain 1.06 %, Temperature 40.0 °C | 17850 psi @Strain 1.06 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 123.56 MPa @Strain 3.77 %, Temperature 90.0 °C | 17921 psi @Strain 3.77 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 124.62 MPa @Strain 3.03 %, Temperature 40.0 °C | 18075 psi @Strain 3.03 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 125.53 MPa @Strain 2.00 %, Temperature 23.0 °C | 18207 psi @Strain 2.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 128.71 MPa @Strain 4.40 %, Temperature 90.0 °C | 18668 psi @Strain 4.40 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 129.09 MPa @Strain 0.940 %, Temperature -20.0 °C | 18723 psi @Strain 0.940 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 130.33 MPa @Strain 1.04 %, Temperature 23.0 °C | 18903 psi @Strain 1.04 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 130.49 MPa @Strain 3.53 %, Temperature 40.0 °C | 18926 psi @Strain 3.53 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 130.66 MPa @Strain 1.16 %, Temperature 0.000 °C | 18951 psi @Strain 1.16 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 131.28 MPa @Strain 1.92 %, Temperature 60.0 °C | 19041 psi @Strain 1.92 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 132.51 MPa @Strain 5.12 %, Temperature 90.0 °C | 19219 psi @Strain 5.12 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 134.28 MPa @Strain 5.95 %, Temperature 90.0 °C | 19476 psi @Strain 5.95 %, Temperature 194 °F | DAM; ISO 11403-1/-2 | |||
| 134.28 MPa @Strain 5.95 %, Temperature 60.0 °C | 19476 psi @Strain 5.95 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 134.79 MPa @Strain 4.06 %, Temperature 40.0 °C | 19550 psi @Strain 4.06 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 136.09 MPa @Strain 2.38 %, Temperature 23.0 °C | 19738 psi @Strain 2.38 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 136.37 MPa @Strain 4.74 %, Temperature 40.0 °C | 19779 psi @Strain 4.74 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 142.18 MPa @Strain 1.33 %, Temperature 40.0 °C | 20622 psi @Strain 1.33 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 144.32 MPa @Strain 2.36 %, Temperature 60.0 °C | 20932 psi @Strain 2.36 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 145.49 MPa @Strain 2.80 %, Temperature 23.0 °C | 21102 psi @Strain 2.80 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 146.31 MPa @Strain 1.37 %, Temperature 0.000 °C | 21221 psi @Strain 1.37 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 147.36 MPa @Strain 1.11 %, Temperature -20.0 °C | 21373 psi @Strain 1.11 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 152.09 MPa @Strain 1.27 %, Temperature 23.0 °C | 22059 psi @Strain 1.27 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 153.31 MPa @Strain 3.26 %, Temperature 23.0 °C | 22236 psi @Strain 3.26 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 155.72 MPa @Strain 2.84 %, Temperature 60.0 °C | 22585 psi @Strain 2.84 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 159.02 MPa @Strain 3.81 %, Temperature 23.0 °C | 23064 psi @Strain 3.81 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 159.75 MPa @Strain 1.64 %, Temperature 40.0 °C | 23170 psi @Strain 1.64 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 160.64 MPa @Strain 4.50 %, Temperature 23.0 °C | 23299 psi @Strain 4.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
| 161 MPa @Strain 1.22 %, Temperature 0.000 °C | 23400 psi @Strain 1.22 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 161.16 MPa @Strain 1.61 %, Temperature 0.000 °C | 23374 psi @Strain 1.61 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 165.25 MPa @Strain 3.39 %, Temperature 60.0 °C | 23968 psi @Strain 3.39 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 165.95 MPa @Strain 1.29 %, Temperature -20.0 °C | 24069 psi @Strain 1.29 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 172.18 MPa @Strain 4.03 %, Temperature 60.0 °C | 24973 psi @Strain 4.03 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 172.91 MPa @Strain 1.58 %, Temperature 23.0 °C | 25079 psi @Strain 1.58 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 174.95 MPa @Strain 4.86 %, Temperature 60.0 °C | 25374 psi @Strain 4.86 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 175.11 MPa @Strain 1.90 %, Temperature 0.000 °C | 25398 psi @Strain 1.90 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 175.73 MPa @Strain 1.99 %, Temperature 40.0 °C | 25488 psi @Strain 1.99 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 183.33 MPa @Strain 1.49 %, Temperature -20.0 °C | 26590 psi @Strain 1.49 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 188.09 MPa @Strain 2.23 %, Temperature 0.000 °C | 27280 psi @Strain 2.23 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 189.83 MPa @Strain 2.42 %, Temperature 40.0 °C | 27533 psi @Strain 2.42 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 192.52 MPa @Strain 1.92 %, Temperature 23.0 °C | 27923 psi @Strain 1.92 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 199.24 MPa @Strain 2.58 %, Temperature 0.000 °C | 28897 psi @Strain 2.58 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 200.07 MPa @Strain 1.73 %, Temperature -20.0 °C | 29018 psi @Strain 1.73 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 201.56 MPa @Strain 2.92 %, Temperature 40.0 °C | 29234 psi @Strain 2.92 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 208.44 MPa @Strain 3.00 %, Temperature 0.000 °C | 30232 psi @Strain 3.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
| 209 MPa @Strain 3.58 %, Temperature 40.0 °C | 30300 psi @Strain 3.58 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 210.17 MPa @Strain 2.35 %, Temperature 23.0 °C | 30483 psi @Strain 2.35 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 214.99 MPa @Strain 1.81 %, Temperature 0.000 °C | 31182 psi @Strain 1.81 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 216.79 MPa @Strain 2.00 %, Temperature -20.0 °C | 31443 psi @Strain 2.00 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 224.63 MPa @Strain 2.84 %, Temperature 23.0 °C | 32580 psi @Strain 2.84 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 231.63 MPa @Strain 2.27 %, Temperature -20.0 °C | 33595 psi @Strain 2.27 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 233.82 MPa @Strain 3.48 %, Temperature 23.0 °C | 33913 psi @Strain 3.48 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 235.08 MPa @Strain 2.14 %, Temperature 0.000 °C | 34096 psi @Strain 2.14 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 244.89 MPa @Strain 2.60 %, Temperature -20.0 °C | 35518 psi @Strain 2.60 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 254 MPa @Strain 2.54 %, Temperature 0.000 °C | 36800 psi @Strain 2.54 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 256.93 MPa @Strain 2.98 %, Temperature -20.0 °C | 37265 psi @Strain 2.98 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 261.67 MPa @Strain 2.98 %, Temperature 0.000 °C | 37952 psi @Strain 2.98 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| Elongation at Break | 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; ASTM D638 | ||
| 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
| 5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 4.415 GPa @Temperature 150 °C | 640.3 ksi @Temperature 302 °F | 50%RH; ISO 527 | ||
| 5.087 GPa @Temperature 120 °C | 737.8 ksi @Temperature 248 °F | 50%RH; ISO 527 | |||
| 5.579 GPa @Temperature 150 °C | 809.2 ksi @Temperature 302 °F | DAM; ISO 527 | |||
| 5.736 GPa @Temperature 90.0 °C | 831.9 ksi @Temperature 194 °F | 50%RH; ISO 527 | |||
| 6.524 GPa @Temperature 120 °C | 946.2 ksi @Temperature 248 °F | DAM; ISO 527 | |||
| 7.964 GPa @Temperature 60.0 °C | 1155 ksi @Temperature 140 °F | 50%RH; ISO 527 | |||
| 7.987 GPa @Temperature 90.0 °C | 1158 ksi @Temperature 194 °F | DAM; ISO 527 | |||
| 8.91 GPa @Temperature 40.0 °C | 1290 ksi @Temperature 104 °F | 50%RH; ISO 527 | |||
| 9.70 GPa @Temperature 23.0 °C | 1410 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 9.707 GPa @Temperature 60.0 °C | 1408 ksi @Temperature 140 °F | DAM; ISO 527 | |||
| 13.02 GPa @Temperature 0.000 °C | 1888 ksi @Temperature 32.0 °F | 50%RH; ISO 527 | |||
| 13.229 GPa @Temperature 40.0 °C | 1918.7 ksi @Temperature 104 °F | DAM; ISO 527 | |||
| 14.5 GPa @Temperature 23.0 °C | 2100 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| 14.544 GPa @Temperature -20.0 °C | 2109.4 ksi @Temperature -4.00 °F | 50%RH; ISO 527 | |||
| 15.659 GPa @Temperature 0.000 °C | 2271.1 ksi @Temperature 32.0 °F | DAM; ISO 527 | |||
| 15.885 GPa @Temperature -20.0 °C | 2303.9 ksi @Temperature -4.00 °F | DAM; ISO 527 | |||
| Flexural Modulus | 7.00 GPa @Temperature 23.0 °C | 1020 ksi @Temperature 73.4 °F | 50%RH; ASTM D790 | ||
| 12.07 GPa @Temperature 23.0 °C | 1751 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| 13.0 GPa @Temperature 23.0 °C | 1890 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Shear Modulus | 0.392 GPa @Temperature 210 °C | 56.9 ksi @Temperature 410 °F | DAM; ISO 6721 | ||
| 0.528 GPa @Temperature 200 °C | 76.6 ksi @Temperature 392 °F | DAM; ISO 6721 | |||
| 0.618 GPa @Temperature 190 °C | 89.6 ksi @Temperature 374 °F | DAM; ISO 6721 | |||
| 0.670 GPa @Temperature 180 °C | 97.2 ksi @Temperature 356 °F | DAM; ISO 6721 | |||
| 0.704 GPa @Temperature 170 °C | 102 ksi @Temperature 338 °F | DAM; ISO 6721 | |||
| 0.731 GPa @Temperature 160 °C | 106 ksi @Temperature 320 °F | DAM; ISO 6721 | |||
| 0.753 GPa @Temperature 150 °C | 109 ksi @Temperature 302 °F | DAM; ISO 6721 | |||
| 0.771 GPa @Temperature 140 °C | 112 ksi @Temperature 284 °F | DAM; ISO 6721 | |||
| 0.785 GPa @Temperature 130 °C | 114 ksi @Temperature 266 °F | DAM; ISO 6721 | |||
| 0.799 GPa @Temperature 120 °C | 116 ksi @Temperature 248 °F | DAM; ISO 6721 | |||
| 0.816 GPa @Temperature 110 °C | 118 ksi @Temperature 230 °F | DAM; ISO 6721 | |||
| 0.840 GPa @Temperature 100 °C | 122 ksi @Temperature 212 °F | DAM; ISO 6721 | |||
| 0.874 GPa @Temperature 90.0 °C | 127 ksi @Temperature 194 °F | DAM; ISO 6721 | |||
| 0.926 GPa @Temperature 80.0 °C | 134 ksi @Temperature 176 °F | DAM; ISO 6721 | |||
| 1.014 GPa @Temperature 70.0 °C | 147.1 ksi @Temperature 158 °F | DAM; ISO 6721 | |||
| 1.176 GPa @Temperature 60.0 °C | 170.6 ksi @Temperature 140 °F | DAM; ISO 6721 | |||
| 1.512 GPa @Temperature 50.0 °C | 219.3 ksi @Temperature 122 °F | DAM; ISO 6721 | |||
| 1.947 GPa @Temperature 40.0 °C | 282.4 ksi @Temperature 104 °F | DAM; ISO 6721 | |||
| 2.124 GPa @Temperature 30.0 °C | 308.1 ksi @Temperature 86.0 °F | DAM; ISO 6721 | |||
| 2.217 GPa @Temperature 20.0 °C | 321.6 ksi @Temperature 68.0 °F | DAM; ISO 6721 | |||
| 2.284 GPa @Temperature 10.0 °C | 331.3 ksi @Temperature 50.0 °F | DAM; ISO 6721 | |||
| 2.321 GPa @Temperature 0.000 °C | 336.6 ksi @Temperature 32.0 °F | DAM; ISO 6721 | |||
| 2.341 GPa @Temperature -10.0 °C | 339.5 ksi @Temperature 14.0 °F | DAM; ISO 6721 | |||
| 2.357 GPa @Temperature -20.0 °C | 341.9 ksi @Temperature -4.00 °F | DAM; ISO 6721 | |||
| 2.38 GPa @Temperature -30.0 °C | 345 ksi @Temperature -22.0 °F | DAM; ISO 6721 | |||
| 2.419 GPa @Temperature -40.0 °C | 350.9 ksi @Temperature -40.0 °F | DAM; ISO 6721 | |||
| 2.488 GPa @Temperature -50.0 °C | 360.9 ksi @Temperature -58.0 °F | DAM; ISO 6721 | |||
| Izod Impact, Notched | 1.85 J/cm @Temperature 23.0 °C | 3.47 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| 2.40 J/cm @Temperature 23.0 °C | 4.50 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D256 | |||
| Izod Impact, Unnotched | 14.9 J/cm @Temperature 23.0 °C | 27.9 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D4812 | ||
| 14.9 J/cm @Temperature 23.0 °C | 27.9 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 15.0 kJ/m² @Temperature -30.0 °C | 7.14 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | ||
| 18.0 kJ/m² @Temperature 23.0 °C | 8.57 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 24.0 kJ/m² @Temperature 23.0 °C | 11.4 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 10.1 J/cm² @Temperature -30.0 °C | 48.1 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | ||
| 11.1 J/cm² @Temperature 23.0 °C | 52.8 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| 11.5 J/cm² @Temperature -30.0 °C | 54.7 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| 11.5 J/cm² @Temperature 23.0 °C | 54.7 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.90 J/cm² @Temperature -30.0 °C | 9.04 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | ||
| 2.00 J/cm² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 2.30 J/cm² @Temperature -30.0 °C | 10.9 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |||
| 2.50 J/cm² @Temperature 23.0 °C | 11.9 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 9400 MPa @Temperature 23.0 °C | 1.36e+6 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 7300 MPa @Temperature 23.0 °C | 1.06e+6 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 100 µm/m-°C @Temperature 23.0 - 55.0 °C | 55.6 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | DAM; ISO 75-1/-2 | ||
| 221 °C | 430 °F | DAM; ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | DAM; ISO 75-1/-2 | ||
| 213 °C | 415 °F | DAM; ASTM D648 | |||
| UL RTI, Electrical | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 270 °C | 518 °F | DAM; Optimum | |||
| 260 - 280 °C | 500 - 536 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Lubricant | DAM | |||
| Appearance | Natural Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | General Purpose | DAM | |||
| Gloss, High | DAM | ||||
| Lubricated | DAM | ||||
| Stiffness, Good | DAM | ||||
| Strength, Good | DAM | ||||
| Surface Finish, Good | DAM | ||||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 6 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA6-GF45< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA6 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA6-GF45 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Appliance Components | DAM | |||
| High Gloss Applications | DAM | ||||
| Industrial Applications | DAM | ||||
| Sporting Goods | DAM | ||||