- 熔体流动速率 [g/10min]: 5.3
- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 2.3
- 拉伸强度 [MPa]: 75.0
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Water Absorption | 2.3 % | 2.3 % | |
| Melt Flow | 5.3 g/10 min @Load 2.16 kg, Temperature 235 °C | 5.3 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min |
| Tensile Modulus | 2.07 GPa | 300 ksi | 1 mm/min |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | 115 °C | 239 °F | 10°C/min |
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |
| Oxygen Index | 26 % | 26 % | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 80 % | 80 % | Mfr. reports 'Transparent' but doesn't quantify. |