- 熔体流动速率 [g/10min]: 2.1
- 密度 [g/cm3]: 1.07
- 吸水率 [%]: 1.4
- 拉伸强度 [MPa]: 50.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in³ | |
| Water Absorption | 1.4 % | 1.4 % | |
| Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 235 °C | 2.1 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | 50 mm/min |
| Elongation at Break | 33 % | 33 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min |
| Tensile Modulus | 2.36 GPa | 342 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 34.1 kV/mm | 866 kV/in | |
| Dissipation Factor | 0.000358 @Frequency 1e+6 Hz | 0.000358 @Frequency 1e+6 Hz | |
| 0.000411 @Frequency 100 Hz | 0.000411 @Frequency 100 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 174 °C | 345 °F | 10°C/min |
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||