- 熔体流动速率 [g/10min]: 6.0
- 拉伸强度 [MPa]: 28.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 27 % | 27 % | 50 mm/min |
| Tensile Modulus | 0.475 GPa | 68.9 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | 4.56 J/cm² | 21.7 ft-lb/in² | Partial Break |
| 0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.14e+14 ohm-cm | 1.14e+14 ohm-cm | |
| Surface Resistance | 7.74e+13 ohm | 7.74e+13 ohm | |
| Dielectric Strength | 40.7 kV/mm | 1030 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 147 µm/m-°C @Temperature 20.0 °C | 81.7 µin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 44.0 °C | 111 °F | |