- 熔体流动速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.15
- 弯曲强度 [MPa]: 154.0
- 热变形温度 [℃]: 175.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 154 MPa | 22300 psi | 5 mm/min |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min |
| Tensile Modulus | 14.0 GPa | 2030 ksi | 1 mm/min |
| Charpy Impact Unnotched | 5.92 J/cm² | 28.2 ft-lb/in² | |
| 5.86 J/cm² @Temperature -30.0 °C | 27.9 ft-lb/in² @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.55 J/cm² | 7.38 ft-lb/in² | |
| 0.910 J/cm² @Temperature -30.0 °C | 4.33 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 400 ohm-cm | 400 ohm-cm | |
| Dielectric Strength | 1.00 kV/mm | 25.4 kV/in | |
| Comparative Tracking Index | 100 V | 100 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature 20.0 °C | 22.2 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 174 °C | 345 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 162 °C | 324 °F | |
| Vicat Softening Point | 170 °C | 338 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||