- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 1.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.60 % | 0.60 % | in normal climate 23°C/50%RH; ISO 62 |
| Water Absorption at Saturation | 1.1 % | 1.1 % | in water at 23°C; ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 120 MPa | 17400 psi | value at 30 sec.; ISO 2039-1 |
| Tensile Strength at Break | 105 MPa | 15200 psi | v = 5 mm/min; ISO 527-2 |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527-2 |
| Tensile Modulus | 6.00 GPa | 870 ksi | ISO 527-2 |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 2.00 J/cm² | 9.52 ft-lb/in² | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz | 4.0 @Frequency 1e+6 Hz | IEC 60250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | in transformer oil; IEC 60243-1 |
| Dissipation Factor | 0.040 @Frequency 1e+6 Hz | 0.040 @Frequency 1e+6 Hz | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 µm/m-°C @Temperature 20.0 °C | 11.1 µin/in-°F @Temperature 68.0 °F | ISO 11359 |
| Thermal Conductivity | 0.160 W/m-K | 1.11 BTU-in/hr-ft²-°F | |
| Melting Point | 178 °C | 352 °F | 10K/min; ISO 3146 |
| Maximum Service Temperature, Air | 150 °C | 302 °F | Short term |
| 160 °C | 320 °F | Long Term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ISO 75-2 |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |
| HB @Thickness 6.00 mm | HB @Thickness 0.236 in | ||