- 密度 [g/cm3]: 1.06
- 吸水率 [%]: 3.5
- 拉伸强度 [MPa]: 75.0
- 热变形温度 [℃]: 145.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in³ | ISO 1183 | ||
| Water Absorption | 3.5 % | 3.5 % | ISO 62 | ||
| Moisture Absorption | 1.50 % | 1.50 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | ISO 294-4, 2577 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 120 MPa | 17400 psi | conditioned; ISO 2039-1 | ||
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | conditioned; ISO 527-1/-2 | ||
| 75.0 MPa | 10900 psi | dry; ISO 527-1/-2 | |||
| Elongation at Break | >= 50 % | >= 50 % | conditioned; ISO 527-1/-2 | ||
| <= 50 % | <= 50 % | dry; ISO 527-1/-2 | |||
| Elongation at Yield | 7.0 % | 7.0 % | dry; ISO 527-1/-2 | ||
| 9.0 % | 9.0 % | conditioned; ISO 527-1/-2 | |||
| Tensile Modulus | 2.20 GPa | 319 ksi | conditioned; ISO 527-1/-2 | ||
| 2.20 GPa | 319 ksi | dry; ISO 527-1/-2 | |||
| Charpy Impact Unnotched | NB | NB | dry; ISO 179/1eU | ||
| NB | NB | conditioned; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| NB @Temperature 30.0 °C | NB @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | dry; ISO 179/1eA | ||
| 0.800 J/cm² | 3.81 ft-lb/in² | conditioned; ISO 179/1eA | |||
| 0.700 J/cm² @Temperature 30.0 °C | 3.33 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
| 0.700 J/cm² @Temperature 30.0 °C | 3.33 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | conditioned; IEC 60243-1 | ||
| Comparative Tracking Index | 600 V | 600 V | conditioned; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1/-2 | ||
| Maximum Service Temperature, Air | 80.0 - 100 °C | 176 - 212 °F | long term; EMS | ||
| 120 °C | 248 °F | short term; EMS | |||
| Transformation Temperature, Tg | 160 °C | 320 °F | 10°C/min; ISO 11357-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Descriptive Properties | |||||
| Automotive | Automotive electr. and electronics, lighting | ||||
| Cooling and climate control | |||||
| Fuel systems | |||||
| Interior | |||||
| Powertrain and Chassis | |||||
| Electricals & Electronics | Cables & Tubes | ||||
| Electrical appliances | |||||
| Electrical equipment | |||||
| Energy distribution | |||||
| Lighting | |||||
| Mobile phones and other portable devices | |||||
| Food contact | EU Requirements | ||||
| FDA | |||||
| Form | Granules | ||||
| Industry & Consumer goods | Heating systems | ||||
| Housewares | |||||
| Hydraulics & Pneumatics | |||||
| Mechanical Engineering | |||||
| Medical devices | |||||
| Power transmission | |||||
| Sanitary, water and gas supply | |||||
| Sports & Leisure | |||||
| Tools & Accessories | |||||
| Medical | FDA | ||||
| USP VI | |||||
| Optics | Lenses | ||||
| Optical components | |||||
| Packaging | Cosmetics / Personal care | ||||
| Medical packaging | |||||
| Non oriented film | |||||
| Processing | Injection Molding | ||||
| Other Extrusion | |||||
| Special Characteristics | Transparent | ||||
| Water Contact | DVGW W270 | ||||
| KTW | |||||
| NSF 61 | |||||
| WRAS | |||||