- 密度 [g/cm3]: 1.01
- 拉伸强度 [MPa]: 41.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | |
| Moisture Absorption at Equilibrium | <= 0.50 % | <= 0.50 % | Humidity Absorption |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 13 % | 13 % | |
| Modulus of Elasticity | 1.30 GPa | 189 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.20 J/cm² | 5.71 ft-lb/in² | |
| 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 3.00e+14 ohm-cm | 3.00e+14 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | |
| 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | ||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | |
| Dissipation Factor | 0.050 @Frequency 1e+6 Hz | 0.050 @Frequency 1e+6 Hz | |
| 0.070 @Frequency 100 Hz | 0.070 @Frequency 100 Hz | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | <= 50.0 µm/m-°C @Temperature 20.0 °C | <= 27.8 µin/in-°F @Temperature 68.0 °F | |
| Vicat Softening Point | 140 °C | 284 °F | 50°C/hr/50 N |
| UL RTI, Electrical | 120 °C | 248 °F | |
| UL RTI, Mechanical with Impact | 85.0 °C | 185 °F | |
| UL RTI, Mechanical without Impact | 95.0 °C | 203 °F | |